Evaluation of electrochemical behavior of the passive film formed on Ni in 1N H3PO4 solution

Nesrine Ramli, Farida Kellou-Kerkouche  (2016)
Article de conférence

This paper focuses on electrochemical studies of nickel oxide, formed on metallic Ni electrode in 1N H3PO4 aqueous solution by means of anodic polarization at various temperatures. Open circuit potential (ocp), potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) and capacitance measurements are the principal techniques which are used. Mott–Schottky analysis shows that the passive film formed on nickel is p-type, corresponding to a preponderance of oxygen vacancies and nickel interstitials in the barrier layer. The acceptor density and flat potential, of the semiconductivepassive layer growing on nickel surface in pho5sphoric acid solution, were determined. Voir les détails

Mots clés : passive film, nickel oxide, Electrochemical impedance spectroscopy, Mott–Schottky.

SURFACE CONDITIONS EFFECT ON THE CORROSION BEHAVIOUR OF STEEL REBAR IN SIMULATED CONCRETE PORE SOLUTION

Somia BELKHIR, Hakim BENSABRA, Noureddine AZZOUZ, Agnieszka FRANCZAK, Omar ABOUBI  (2016)
Article de conférence

In order to study a surface conditions effect on the corrosion behaviour of steel rebar, electrochemical tests were carried out in simulated concrete pore solution using samples with two different surfaces: polished and corroded (as received). The obtained results show that the oxide layer has a negative effect on the corrosion behaviour of reinforcement steel. This effect can be explained by the fact that the oxides provoke a decrease of the electrolyte resistance at the metal/concrete interface and reduce the re-passivating ability. In addition, the oxide layer acts as a physical barrier against the diffusion of hydroxyl ions, which prevents the realkalinization phenomenon. Voir les détails

Mots clés : corrosion, concrete, steel, chloride, rust.

Synthesis of Nano Particles CuO by sol-gel process and studies their Characterizations Structural

Rabie Bacha, Abderrahmane Chaieb, A. Bouchtout, A. Chari  (2016)
Article de conférence

The aim of this work is synthesis and characterization of the copper oxide powders “CuO” and its composite thin film of (CuO/PMMA), by (sol-gel) process (wet-chemistry route, using (Cu (CH3COO) 2, H2O), as precursor and DMF (CH3) NC (OH), as solvent, the obtained powder has undergone a heat treatment annealing to 450°C. The structural analysis by X-Ray diffraction and the Fourier transform infrared (FTIR) reveal the single phase monoclinic structure of CuO, the average crystallite size of the powder annealed to 450 C° is 16,76nm. Voir les détails

Mots clés : CuO, CuO/PMMA, thin film, powders, (sol-gel) process, structural analysis.

Fabrication and characterization of pure ZnO thin films deposited by Sol – gel method

S. Haya, O. Halimi, M. Sebais, B. Boudine, O. BRAHMIA  (2016)
Article de conférence

ZnO thin films were prepared via Sol-gel method and were deposited on an ordinary glass substrate using dip coating technique. These films undergo optical annealing using UV irradiation during 2 hours. The starting materials used were zinc acetate dehydrate, 2-methoxyethanol which was used as solvent as well as the mono-ethanolamine (MEA) as stabilizer. Xraydiffraction study shows that all the films prepared in this work have a preferential orientation situated at 34° and correspond to (002) plan of the hexagonal Wurtzite structure, with lattice constants a = b = 3.02 Å, c = 5.20 Å. The optical band gap energy of the thin films was found to be a direct allowed transition ~3.23 eV. These values belong to the blue shift absorbance. Moreover, the photoluminescence measurement reveals that the prepared samples exhibit intense emission band in the visible and near UV. This observation led us to practical applications in the area of optoelectronic. Voir les détails

Mots clés : Photoluminescence, band gap, ZnO, sol-gel method

Time-varying ultimate strength of aging sheet pile considering corrosion effect

Balegh Benamar, Trouzine Habib  (2016)
Article de conférence

Steel Sheet pile walls are widely used in excavation support systems, cofferdams, cut-off walls under dams, slope stabilization, water front structures, and floodwall. Corrosion in sheet pile leads to severe degradation processes which usually affect both the ultimate and serviceability limit state performance of the structure. Recent developments in mathematical modeling strategies, in association with in situ thickness measurements, have significantly enhanced the qualitative understanding of the corrosion processes at various locations within marine structures. A comprehensive mathematical model is developed that allows capturing all the main effects of corrosion. Voir les détails

Mots clés : Sheet pile, corrosion, Mathematical, modeling

ILLUSTRATION OF SQUAR-WAVE VOLTAMMETRY AS AN EFFICIENTANALYTICAL METHOD FOR NANOMOL AMOUNT HIGH DETECTION OF HEAVY METALS FOR ENVIRONMENTAL APPLICATIONS

Sakhraoui Houssem Eddine El yamine, Maouche Naima  (2016)
Article de conférence

Square wave voltammetry (SWV) has been widely used in the development of electrochemical sensors and biosensors in recent years due to its high selectivity and sensitivity. It is of great interest and importance to rapidly and sensitively detect disease-related biomarkers, environmental pollutants (e.g., heavy metals and other chemical contaminants), which are severely detrimental to human and animal life and the environment as a whole. Voir les détails

Mots clés : Square wave voltammetry, Molecularly imprinted, Molecularly imprinted polymers, Detection, environment

Improvement in Nano-hardness and Corrosion Resistance of of XC48 Samples by Plasma Immersion Ion Implantation

M. M. ALIM, N. Saoula, R. TADJINE, A. Keffous, M. Kechouane  (2016)
Article de conférence

In this work, Nitrogen Plasma Immersion Ion Implantation (PIII) treatment of (XC48) Carbon steel was performed in a vacuum chamber with an inductive RF source (l3.56 MHz) at low pressure in order to investigate the influence of the process conditions on the corrosion properties of this studied material. The X-rays diffraction analysis revealed the presence of several nitride phases (Fe3N and FeN) formed onto implanted samples. The mechanical characterization of the processed samples showed an increase of 450 % in the nanohardness.A low corrosion rate is obtained denoting an improvement in the corrosion resistance behavior. These results are particularly interesting since they were obtained for relatively low bias voltages and processing time. Voir les détails

Mots clés : Plasma nitriding, Low Carbon Steel, Nanohardness, corrosion resistance, Negative DC bias voltage

The comparative study between the inhibitive effect of sodium molibdate and sodium vanadate on the corrosion behaviour of aluminium alloy in chloride medium

Meryem ACILA, Hakim BENSABRA, Noureddine AZZOUZ, Somia BELKHIR  (2016)
Article de conférence

The effect of molybdate and vanadate inhibitor ions on the corrosion of aluminium alloy in near-neutral chloride solution has been studied using measurements of the open circuit potential and its variation with time, electrochemical impedance measurements and polarization curves. In addition, scanning electron microscopy coupled with energy dispersive spectroscopy and X-ray photoelectrons were used for surface analysis. The results show that both inhibitors present an interesting protective effect against pitting corrosion of aluminum. However the effect of molybdate is more significant than the one of vanadate. This inhibitive effect is reflected through the substantial reduction of both the rate of pit nucleation and the current rise characterizing the pit propagation progress. Voir les détails

Mots clés : corrosion, aluminum, chlorides, inhibitors, molybdate, vanadate

Elaboration and characterization of nanosized RuO2-TiO2 powder by Sol Gel route

F. Mousli, A. Kadri, N. Benbrahim, A. Chaouchi  (2016)
Article de conférence

Mixed metal oxide, RuO2-TiO2 powders were successfully synthesized via a sol gel method and reflux process by using hydrolysis of titanium oxide nanopowders (prepared in the first stage by sol gel route) with its mixture anatase and rutile phases and RuCl3 as rhutenium source in water and alcohol. Nanopowders thus prepared are characterized by X-ray diffraction, UV solid, SEM, ATG and FT-IR techniques. The XRD spectrum confirms the complete conversion of RuCl3 to RuO2 with the presence of TiO2 in its anatase phase only, which is due to the conversion of rutile TiO2 to anatase TiO2. The crystallite size calculated from Debye-Scherrer’s formula is 9 nm. UV solid study show that the characteristic absorption bands of TiO has a low intensity; this is only due to the strong absorption of RuO2 by contribution to titanium oxide. It is reported an increase in absorption intensity with the RuO2 content. This can be attributed to the external effect of resonance related to the excitation of electron collective oscillations in the RuO2 nanoparticles by the electric field of the electromagnetic wave. Voir les détails

Mots clés : nanopowders, sol gel, RuO2-TiO2

Steel XC38 protection against corrosion by an organic compound (DHASC) in hydrochloric acid medium

Leila Hasniou, Saleh Chafaa, Amel Djdouani, Leila LAMIRI, Linda Djaouane, Radhia YEKHLEF  (2016)
Article de conférence

Corrosion in industrial environments is a major factor limiting the lifespan of materials, causing many replacement costs and lost productivity. For a judicious selection of materials in particularly aggressive environments, one must often use standardized laboratory tests and / or factory whose validity and reliability have not always been clearly demonstrated. Corrosion inhibitors are a means of struggle against corrosion of metals and alloys relatively recent. The originality of this method is the fact that the anti-corrosion treatment is not done on the metal itself but through the corrosive environment. The inhibitor molecules may act on different mechanisms, thus giving them dependent inhibition material performance and study environment. In this work we have synthesized and characterized a novel organic compound (DHASC) To identify it, we appealed to the physicochemical methods of analysis: IR, UV-Vis, NMR 1H and voltammetry cyclic organic medium (DMF-Bu4NPF6 0.1M) was platinum electrode. The study of the inhibitory effect of the ligand on the corrosion of carbon steel X52 in hydrochloric acid medium and in the presents inhibition character. The inhibitory efficacy in hydrochloric acid medium, it reaches 69% at a concentration of 10-5M. The application of this new ligand synthesized in everyday life, the water treatment industry in the fight against corrosion. Voir les détails

Mots clés : Corrosion Protection Steel XC38, inhibitor