Effect of cold rolling on the recrystallization of 904L austenitic stainless steel

Type : Article de conférence
Auteur(s) :  Lyacine RABAHI, Brahim MEHDI, Idir HADJI, Riad BADJI, Nabil KHERROUBA
Année :  2019
Domaine : Sciences des matériaux
Conférence: 5th international conference on advances in mechanical engineering ICAME2019
Résumé en PDF :  (résumé en pdf)
Fulltext en PDF :  (.pdf)
Mots clés :  recrystallization, 904L, Cold rolling, DSC

Résumé : 

The aim of this work is to study the recrystallization in the 904L austenitic stainless steel, which underwent a cold rolling with two different deformation amounts (50 and 90%). DSC tests have been conducted to determine the temperature range of the recrystallization. It was found that reducing the deformation amount slightly delays the recrystallization. The microstructure of the as-received alloy consists of austenitic grains recognized by the twins they contain. The deformation induced a corrugated microstructure with the presence of ribs. The XRD analysis confirmed that only γ phase peaks were present in the as-received alloy and showed that the deformation induced the extinction of γ phase peaks and the apparition of α phase peaks.